Superconducting Ceramics

In 1986, Georg Bednorz and K. Alex Muller discovered superconductivity
at much higher temperatures than had previously been thought possible,
and in an oxide rather than a metal. Since this discovery, several new
superconducting compounds have been found. Many of their
superconducting properties have been measured and the first steps taken
towards their utilization in superconducting electronics and magnet
applications. However, the subject of oxide superconductors is far from
mature with a number of key issues yet to be resolved. The bulk of the
research performed so far has been devoted to the properties of the yttrium
barium cuprate superconductor.

The structure of yttrium barium cuprate (YBa2Cu3O7-x) is rather
complicated because it contains several inequivalent copper sites and can
exhibit a wide range of oxygen contents, ranging from YBa2Cu3O6 to
YBa2Cu3O7. The fully oxygenated compound, YBa2Cu3O7,
               has a orthorhombic unit cell. Two layers of Cu-O,
having a square-planar arrangement, are separated by a layer of Y ions.
The second type of copper site is also four coordinated with oxygen, but
can be thought of as belonging to a chain lying along the b-axis of the unit
cell. In both the planar and chain configurations, the Cu-O distance is
small, suggesting covalent bonding in the chain, as well as in the Cu-O
plane. The fully oxygen-deficient compound, YBa2Cu3O6, contains
fewer oxygen atom per unit cell. Its structure is the same as that of
YBa2Cu3O7 but with the oxygen removed for the Cu-O chains in the
b-direction, so resulting in a tetragonal unit cell. This compound is not
superconducting. The superconducting transition temperature is dependent
on the oxygen stoichiometry of the yttrium barium cuprate, and steadily
decreases with reduction in the oxygen content until a metal-insulator
transition is reached, at a composition approximating to YBa2Cu3O6.4.
As oxygen is taken from the compound, it is removed from the chain sites
to create oxygen vacancies to give a structure intermediate between that of
YBa2Cu3O7 and YBa2Cu3O6 (YBa2Cu3O7-x).

--

--